Layered alumina-based abrasive grit, abrasive products, and methods

ABSTRACT

Alumina-based abrasive material having at least an internal layer is provided. Preferably, the abrasive material results from co-extrusion of at least two different sols. In some preferred processing, steps to provide multiple internal layers are conducted.

FIELD OF THE INVENTION

The present invention concerns alumina-based abrasive grit material;methods of preparing such abrasive grit material; and, productsincorporating the abrasive grit material. In general, abrasive grits asdescribed herein have internal stratified or layered structures. Theabrasive grits can be made using sol-gel techniques.

BACKGROUND OF THE INVENTION

Abrasive grits or particles have long been employed in abrasiveproducts. These abrasive products include bonded abrasives (e.g.,grinding wheels), coated abrasives, and nonwoven abrasives. Preferredabrasive grit is typically tough, hard, and chemically resistant to theworkpiece being abraded. A "tough" abrasive grit is generally strong andfracture resistant. A "hard" abrasive grit generally resists yielding ordulling from the forces of grinding. When the abrasive grit does yieldor dull, decreased abrading performance typically results.

One common type of aggressive abrasive grit, known as fused alumina, isformed by heating a source of aluminum oxide to a molten state, rapidlycooling and then crushing. This type of abrasive grit is hard, tough,and chemically resistant.

A more recently developed type of abrasive grit is often referred to asalpha alumina-based ceramic abrasive grit. This type of abrasive gritcan be made by a sol-gel process, wherein, for example, a dispersioncomprising a liquid medium (typically water), alpha alumina monohydrate,and optional additives such as metal oxide precursors (e.g., magnesiumnitrate), is dried, crushed, calcined, and then sintered. The resultantceramic abrasive grit is typically tougher than the fused alumina grit,and typically exhibits superior performance in abrading operations.

Abrasive products containing sol-gel based alpha alumina grits orparticles have been in commercial use for up to 15 years. During thistime, there have been numerous improvements made to the alumina abrasivegrits or particles. Some of these improvements concern modifications tothe crystal structure (referred to as the microstructure) of the alphaalumina crystals which form the abrasive grits or particles. Theabrasives industry has, in general, been seeking higher performingalumina abrasive particles to incorporate into abrasive articles.

SUMMARY OF THE INVENTION

According to the present invention there is provided alumina-basedabrasive grit having internal stratified or layered structure.Generally, at least one internal layer is found in the abrasive grit.Techniques for preparing abrasive grits having multiple internal layersare provided.

The internal layering may comprise alternating layers of two differentmaterials, or multiple layers of more than two types of materials. Thelayering, in preferred constructions, results from co-extrusionprocesses. The co-extrusion process can be combined with stratifying ormixing, to achieve still more layers.

In some applications it may be desired to co-extrude two materials,which although prepared differently, may result in somewhat the samemicrostructure and chemical structure. Additionally, in some instances,advantages may be seen from co-extruding two identical materials, evenin situations wherein no difference can be observed between the twostructures in the final produce.

General techniques of processing, according to the present invention,comprise co-extruding to form a co-extrudate, with or without a mixingstep. The co-extrudate is generally dried and fired to form ceramicproduct. Typically, during processing, the co-extrudate can be crushed,broken or cut to form either a randomly shaped or a shaped particle, andin some instances sizing will be involved in order to obtain a preferredgrade of abrasive grit.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic view of an abrasive grit of the present invention.

FIG. 2 is a cross-section of the abrasive grit of FIG. 1 taken alongline 2--2.

FIG. 3 is a cross-section of the abrasive grit of FIG. 2 taken alongline 3--3.

FIGS. 4 through 8 are photomicrographs of abrasive grits made accordingto the method of the present invention.

FIG. 9 is a schematic of a process for production of abrasive gritsaccording to certain applications of the present invention.

FIG. 10 is a schematic of a process for production of abrasive gritsaccording to certain alternate applications of the present invention.

FIG. 11 is a schematic of a process for production of abrasive gritsaccording to certain applications of the techniques of the presentinvention.

FIG. 12 is a schematic cross section view of a coated abrasive articleincorporating abrasive grits according to certain applications of thepresent invention. FIG. 13 is a schematic depiction of a bonded abrasivearticle incorporating abrasive grits according to certain applicationsof the present invention.

FIG. 14 is an enlarged schematic close-up view of a non-woven abrasivearticle incorporating abrasive grits according to certain applicationsof the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT Selected Definitions

The term "abrasive grit" or "abrasive particle" as used herein refers toceramic bodies used for abrading, cutting, smoothing, and/or polishing.Typically, abrasive grits or particles, for this patent application,range from 30 to 5000 micrometers in size (largest dimension).Generally, abrasive grits or particles are sized or graded, forcommercial use or sale. The grades are generally defined by sizing withscreens. The screen or grades are defined in a variety of manners, andby various standards organizations. In the United States, typically ANSI(the American National Standards Institute) standards are used. Alsocommonly used are FEPA (Federation of European Producers of Abrasives)and JIS (Japanese International System) grading systems. Common grades(ANSI) are 24, 36, 50, 80, 100, 120, 150, 180, 220, 240, 320 and 400.The number with respect to an ANSI grade refers to a distribution ofparticle sizes as defined in ASNI standard B74.18. The standards, forexample ANSI standards, generally define grades with respect to somepercentage of grit population within a size range, and a limit on theamount of grits outside of the defined size. ANSI 320 generallycorresponds to grits which have a largest dimension of about 40-45micrometers; and ANSI 120 generally refers to grits which have a largestdimension of about 150 micrometers. A grade may be defined as "+80-120"meaning that the material is one which will pass through a number 80screen (USA Standard Testing Sieves, American Society for Testing andMaterials E-11 Specification), but which does not pass through a number120 screen.

The term "internal layer" as used herein refers to a region of ceramicmaterial present in the referenced ceramic body, for example, anabrasive grit. In order to comprise an "internal layer", the region ofceramic material, in three dimensions, should exhibit the followingcharacteristics: (1) it should be present within the ceramic body suchthat it is bounded on two opposite sides by ceramic material, typically"densified" ceramic material; (2) when a selected cross-section is takenthrough the layer, the "artifact" of the layer (or the layer edge)viewable in the cross-section must extend over a length of at least 1micrometer; and, (3) when it is viewed in a direction orthogonal to thepreviously mentioned selected cross-section (either in cross-section orupon edge viewing) the artifact of the layer viewable should extend overa length of at least 1 micrometer. Alternately stated an "internallayer" has a dimension of at least 1 micrometer in two (orthogonal)directions.

As used herein, the term "internal layer edge", with reference toviewing in a cross-section, refers to an artifact of the identifiedlayer viewable in the cross-section. To qualify as an "internal layeredge", the artifact viewable in the cross-section must extendcontinuously (i.e., without a gap or break) a distance of at least 1micrometer.

As used herein, the term "cross-section" refers to a cut, polished, orotherwise prepared surface of a ceramic body or abrasive grit whichtypifies (or represents) the constituents of the grit through its depthin a selected direction. A typical method of preparing a cross-sectionof an abrasive grit is as follows. The abrasive would be prepared bymounting the grits in a mounting material, for example, EPOMET® (&mounting resin available from Buehler, Ltd., Lake Bluff, Ill. The gritsand mounting material are formed into a cylindrical slot measuring about1.0 inch (2.54 cm) in diameter and 0.75 inches (1.91 cm) tall. Themounted sample is polished using an EPOMET® polisher and METADI® diamondslurries, both from Buehler, to obtain polished cross-sections andsamples. The final polishing step uses one micrometer diameter slurry.The final surface finish of this sample would be essentially free ofgouges and scratches when viewed using a light microscope at 100×. Toobtain a cross-section orthogonal to a first cross-section, the polishedgrits are removed from the cylindrical slot by slicing through the slotusing a diamond saw parallel to the polished surface to obtain a waferabout 1 inch in (2.54 cm) diameter and about 0.25 inch (0.64 cm) thick.A segment of the wafer is cut perpendicular to the polished surface. Thesurface is placed upright in a mold or press so that the polished crosssection is parallel to the mold wall; the cross-section again beingmounted in EPOMET® to form a cylindrical slot (with the originalpolished surface parallel to the wall of the slot). The molded sample ispolished as before to form a polished surface perpendicular to theoriginal polished surface. These techniques for cross-sectioning areversions of well-known and widely used polishing and cross-sectioningtechniques in the abrasives industry. Any of the conventional, known,techniques are suitable. The above specification was presented as anexample.

As used herein, the term "at least one" when used in connection with theterm "cross-section" is meant to only refer to at least one possibleselected cross-section. It is not meant to indicate that all possibleselected cross sections would exhibit the feature recited. To qualify asan "at least one" cross-section, the cross-section must be taken at anangle such that it indicates completely, in thickness, both the internallayer and at least those regions of ceramic material immediatelyadjacent the selected internal layer on opposite sides thereof Toqualify as a "cross-section" in this context, the cut or cross-sectionneed not be taken through all layers, in a multilayered system. It isalso not a criterion, for a cut to qualify as a cross-section, that thecut be taken perfectly perpendicularly to a plane of extension, or asurface of extension, of the internal layer. Cross-sectioning at anangle to the extension of an internal layer qualifies, as long as theangle is sufficient and appropriate to at least cut through the completedepth of extension of the two opposite portions or regions of ceramicmaterial immediately adjacent the artifact of the first internal layer,when examined along the cross-section.

When viewed in cross-section, the first internal layer edge will beconsidered "contiguous", with respect to an adjoining region of ceramicmaterial immediately adjacent, if no separation between the first layerand the adjoining region along the line of contact (or interface betweenthe two regions) is viewable in the cross-section. An adjacent extensionof the regions or layers will sometimes be referred to herein as"continuous and contiguous" if it is not only contiguous, but there arealso no gaps or lack of continuity in either one or the two adjoininglayers along the line of contact. As a point of reference for clarity,the interface between an autogenously bonded particulate coating on anabrasive core does not typically qualify as "continuous and contiguous"because gaps in the coating are typically observed in the cross-section.

Herein, when a layer or layer edge is referenced as having a "continuousextension" when viewed in a cross-section, it is meant that thelongitudinal extension of the layer edge, in the cross-section, extendscontinuously and without break. For example, if reference is made to acontinuous extension of at least 30 micrometers, it is meant that thelayer edge, when viewed in the cross-section, extends uninterrupted bygaps for a distance of at least 30 micrometers. A "continuous" extensionmay be straight or have curves, folds, bends or nodes in it.

Herein when a material is characterized by the term "alumina-based", itis meant to refer to the characterized material comprising at least 50%by weight Al₂ O₃ on a theoretical oxides basis. The term "alumina-based"may be used in reference to a particular layer or region alone, or to anoverall grit. A conclusion that a referenced material is "alumina-based"can, in some instances, be derived from: (a) analytical measurement; or(b) calculation based upon starting materials; or (c) both.

Herein the term "greatest dimension of width" when used in reference toan abrasive grit, when viewed in cross-section, refers to the longestdimension, when measured outer edge to outer edge across the abrasivegrit in the selected cross-sectional view. There is no requirement inconnection with this definition that the cross-section be taken suchthat the largest dimension of the overall abrasive grit is reflectedtherein. As a theoretical example: if the abrasive grit were a perfect,long, cylinder, and the cross-section were taken perpendicularly to alongitudinal axis, and parallel to the end surfaces, the "greaterdimension of width" for the view would be the cylinder diameter, inspite of the fact that the largest dimension of the selected cylinder isits length along the longitudinal axis.

Herein the term "outer periphery" when used to define a portion of anabrasive grit, refers to an outermost surface or edge of the abrasivegrit. If the abrasive grit is a grit which is "coated", the term "outerperiphery" is meant to refer to the outer surface of the coating.

Herein when it is said that two regions, layers, portions or phasesdiffer from one another with respect to "microstructure" it is meantthat there is some difference in the arrangement, shape, size or patternof particles, crystals or constituents between the two regions, layers,portions or phases being compared, as seen in cross-section visually orwith the aid of some microscopy technique. For example, if a densifiednucleated internal layer is bounded by a densified non-nucleated ceramicmaterial, a thermally etched (at about 1250° C. for 20-30 minutes)cross-section would typically show a visual difference between theregions when observed by scanning electron microscopy (SEM).

Herein the term "densified" when used in reference to a portion of anabrasive grit, means that when the abrasive grit (when viewed incross-section) does not appear to absorb a significant amount of reddye. A useable red dye test for determining densification is as follows.A drop of red dye ("P303 A Penetrant" from Uresco Androx of Ceritos,Calif., for example) is placed onto a polished cross-section of theabrasive grit exhibiting internal layers. The dye is then washed awaywith water. Densified ceramic material will not absorb a significantamount of dye whereas non-densified ceramic material will absorb the dyeand will retain a reddish or pink hue. It is noted that in general, inthe abrasives industry, hardness or microhardness tests are used toevaluate theoretical density of grits, and thus extent of densification.

Herein when it is said that two regions, layers, portions or phasesdiffer from one another with respect to "composition" it is meant thatone is able to detect differing amounts of elements or ingredientsthrough imaging or microspectroscopic techniques involving one or moreof: back-scattered electron imaging; energy dispersive x-raymicroanalysis; electron energy loss spectroscopy (EELS);electronmicroprobe; or Fourier Transform Infrared spectroscopy (FTIR).Alternatively, a difference in composition can typically be inferredfrom knowledge that the layers were derived from two or morecompositions which differed in ingredients in some manner.

Herein when it is said that two layers, regions, portions or phases are"indistinguishable" from one another with respect to crystallinestructure, it is meant that when viewed in cross-section, visually or bythe use of light or electron microscopy techniques, the microstructuresof the two layers, regions, portions or phases being compared cannot bevisually distinguished with respect microstructure characteristics. Thiscan typically be inferred if the two regions were made from the samecomposition.

Herein when it is said that two layers, regions, portions or phases are"indistinguishable" from one another with respect to composition, it ismeant that one is unable to detect differing amounts of elements oringredients by imaging or microspectroscopic techniques such as:back-scattered electron imaging; energy dispersive x-ray microanalysis;electron energy loss spectroscopy (EELS); electron microprobe; andFourier Transform Infrared spectroscopy (FTIR). This can typically beinferred if the two regions were made from the same composition.

General Principles

In general, abrasive grits according to the present invention havestructures including an internal layer. In many instances, multipleinternal layers will be present. Hereinbelow, detailed description isprovided concerning creation, identification and characterization of theinternal layer structure. In general, abrasive grits having internallayers can be identified either by: artifacts viewable or otherwisedetectable in cross-sections; or, inference from the processingtechnique used. The presence of the internal layers will, in general,readily result from preferred methods of preparation described herein.

Typical preferred processing, to generate internal layered structuresaccording to the present disclosure, will comprise processing in which,during the processing, there is a co-extrusion of two or morecompositions, such as sols. The co-extrusion step may be continuous orintermittent. Multiple layered stratified systems can be generated bymultiple extrusions or by incorporating a step of mixing with theco-extrusion, as described below. Each of the two or more solcompositions which are co-extruded may comprise any of the following:

1. aluminum oxide hydrate sols or sol-gel compositions;

2. alpha alumina sols or sol-gel compositions; for exampleboehmite-based compositions;

3. transitional alumina powder compositions;

4. solutions of aluminum oxide precursor; or

5. hybrid compositions containing two or more of the above.

In general, except for the step of co-extruding, the techniques used toprepare the abrasive grit may involve conventional processing techniquesas described for example in U.S. Pat. Nos. 4,314,827 (Leitheiser);4,881,951 (Wood); 4,770,671 (Monroe); 4,744,802 (Schwabel); 4,623,364(Cottringer et al.), and 5,227,104 (Bauer). The complete disclosures ofthese references are incorporated herein by reference.

The Layered Abrasive Grit Structures

Alumina-based abrasive grits according to the present invention includelayered structures. Typically the grits comprise ceramic particlesincluding at least one alumina-based internal layer. In typical gritsthe referenced alumina-based internal layer will have a first dimensionof at least 10 micrometers (typically at least 30 micrometers and mosttypically at least 50 micrometers) and a second dimension (orthogonal tothe first) of at least 10 micrometers, again typically at least 30micrometers and most typically at least 50 micrometers. In manyinstances, the layer will extend completely across the grits, whenviewed in cross-section. For many grits the existence of such aninternal layer can be confirmed by evaluating layer artifacts, inpolished cross-sections.

In general, this will be understood by reference to the schematics ofFIGS. 1, 2 and 3. In FIG. 1 a schematic representation is provided of aselected (hypothetical) grit. In FIG. 2 a schematic representation of apolished surface cross-section taken generally along section line 2--2illustrated in FIG. 1, is depicted. In FIG. 3 a cross-section takenalong section line 3--3 illustrated in FIG. 2, is shown.

In FIG. 1, artifacts of the multiple layer are viewable from the sideedge. The particular grit shown exhibits distinct layers in the viewselected. Of the layers, ten layers would comprise internal layersaccording to the general definitions herein (assuming that the scaleused is appropriate). Assume that the layers for the schematic of FIG.1, comprise two different materials. More specifically the top layer inthe picture, and alternating layers from there (i.e., layers 3, 5, 7,and 9 counting down from the top) comprise the first material; andlayers 2, 4, 6, 8, 10 and 12 counting from the top, comprise the secondmaterial. Note that the layers generally extend completely across thegrit. For purposes of example, assume that the materials differ only inthat the first ceramic layers resulted from extruding a material with anucleating agent therein; and, the second ceramic layers resulted fromextruding a composition which did not include a nucleating agent.

In FIGS. 2 and 3, cross-sectional artifacts of the internal layers areviewable. As the figures indicate, in general as a result of the mannerin which the layers are formed, i.e., typically co-extrusion, the layersreflect contours, without spacing. For example, in FIG. 2, the layernumbered 4 includes a node which encroaches on the layer numbered 5. Anode is a fold or bend in the layer which formed from pressure (flow)differentials during co-extrusion. What is significant, is that adjacentlayers, numbered 4, 3, and 2, include analogous nodes.

Referring to FIGS. 2 and 3, the artifacts viewable are layer edges. Notethat the layer edges may be orthogonal to layer extension through theassociated portion of the grit 10, or they may be at an angle. The angleselected for the cross-section is relatively unimportant, as long as itreflects the presence or absence of adjacent layers to the internallayers selected for viewing. For example, layers numbered 1 and 3 areadjacent to, and on opposite sides of, the internal layer numbered 2.

Structure similar to that shown in FIG. 2 reflects "continuous" and"contiguous" layers. With respect to the continuity (continuous nature)of the layer, reference is made, for example, to layers numbered 2, 3,and 4. Each edge of the layer numbered 3 is continuous in extension withthe layers numbers 2 and 4 completely across the cross-section, i.e.,from the left side of the grit to the right side. That is, that while itdoes include bends, folds, and curves therein, it does not includebreaks or spaces. Further, the layer numbered 3 is contiguous withlayers 2 and 4, when viewed in the cross-section. That is, there are nospaces or gaps between these layers; i.e., they do not separate. Also,both are continuous in their respective extensions along the viewedinterface.

Structures such as those schematically represented in FIGS. 1-3, canreadily be obtained using co-extrusion techniques described hereinbelow.The number of layers viewable in any given abrasive grit resulting fromthe process will be determined, among other things, by the following:the number of layers co-extruded; the extent of mixing of theco-extrusion; and, the size of particles to which the extrusion isground or broken. Not every grit resulting from a co-extrusion processwill necessarily reflect all layers resulting from the co-extrusion ormixing of the co-extrusion. This is at least because during the breakingand grinding processes the grits may be fragmented to dimensions smallerthan would reflect all layers from processing. However, typically ifco-extrusion processes described herein are used, and the grits examinedhave a size (average largest dimension) of at least 30 (typically atleast 50, often at least 70, and in many instances greater than 100)micrometers, at least one internal layer will be readily detectable inat least one selected cross-section.

Of course the extent to which the artifacts of the layers can be viewed,will depend upon the cross-section selected. Not every possiblecross-section will reflect the structure of an internal layer. Across-section could be taken, for example, at an angle through a gritsuch that the cross-sectioning is only through one layer. This does notmean that the grit does not possess an internal layer, but rather simplythat the cross-section chosen was inappropriate for viewing or detectingthe internal layer.

If, during co-extrusion, intermittence in extrusion of one or more ofthe co-extruded materials occurs, the product which results may have alack of continuous nature to the internal layers. For example, not everyselected internal layer would be continuously bounded on a side by aselected layer. This is logical, since, during the co-extrusion,extrusion of one of the layers would have been interrupted, whileanother layer continues to extrude.

In general, when abrasive grits are made according to the extrusion orco-extrusion processes described herein, they may sometimes be referredto as "sol-gel" abrasive grits or particles. By this it is meant thatwhat is extruded or co-extruded comprises, at least in part, a sol orsol-gel composition as described herein.

Attention is directed to FIG. 4. FIG. 4 is a photograph, the image beingtaken by light microscopy, of a co-extrusion product according toExample 2, fired but not crushed or ground. Note the 0.50 mm, or 500micrometer, scale. The rods, which result from the co-extrusion, showclearly the stratified or multilayered construction. The rods of FIG. 4are the co-extruded product after the drying, calcining, and sinteringsteps described. Typically, for manufacture of abrasive grits, the rodsshown in FIG. 4 would have been crushed or broken into finer grits orparticles, before sintering, which would then (after firing) be sized orclassified according to grades for use or sale As is apparent from thedescription of Example 2, the co-extrusion involved two differentsol-gel compositions, with folding to generate the multiple layeredstructure.

In FIG. 5, a cross-sectional view, prepared as described herein, rodsillustrated in FIG. 4, is shown. Note the 0.25 mm (250 micrometer)scale. One can see the multiple layers clearly in the two polishedcross-sections viewable. In the one in the lower left-hand corner of thepicture, one can see that the multiple layers are not "flat" or"straight". Rather, they fold, bend, or wave as they pass from one sideof the cross-section to the other. Note that layers on opposite sides ofany selected internal layer tend to follow the same contour. Also notethe continuity of the various internal layers. That is, they generallyextend continuously and uninterrupted across large parts of thecross-section.

In general, when rods according to FIGS. 4 and 5 are crushed (eitherbefore or after sintering) into abrasive grits or particles, and aresized, the resultant abrasive grits or particles will exhibit, incross-section, features analogous to those viewable for the rods. Ofcourse the grits would typically be substantially smaller, with respectto largest dimension, than the rods from which they are formed.

Attention is now directed to FIG. 6. In FIG. 6, rods similar to thoseshown in FIG. 4 are depicted in cross-section. However, especially notethe rod in the upper right-hand corner of FIG. 6. This rod has beencross-sectioned twice, similarly to the schematic of FIG. 3, and isviewed generally in perspective, so that one can see around the "corner"of the cross-section. From this it will be apparent that the artifactsviewable in the cross-section, for example, the dark lines, are theartifacts of internal layers since the layers can be traced "around" the"corner" and down or across the orthogonal cross-section. That is, allthree (orthogonal) dimensions of the layer artifact can be viewed(length, width, thickness). From a view similar to that shown in FIG. 6,it is apparent that the structure evaluated is a stratified or layeredstructure. With respect to FIG. 6, note the 0.25 mm (250 micrometer)scale.

Attention is now directed to FIG. 7. FIG. 7 is a high magnificationphotomicrograph taken using back scattered electron imaging showing aninterface between two co-extruded phases in a rod of the type indicatedgenerally in FIGS. 4-6. The phase on the left-hand portion of FIG. 7 isa phase resulting from nucleating with iron oxide; and, the phase on theright-hand portion is a "cellular" phase which results from an extrudedphase that did not include iron oxide nucleating agent. In general, asis characterized herein, there is "intimate" contact between the twophases in the center portion of the Figure. That is, the phases do notseparate from one another. With respect to FIG. 7, note the 1 micrometerscale in the lower right-hand corner of the photograph.

Attention is now directed to FIG. 8. FIG. 8 is a photomicrograph in aperspective view of another embodiment of abrasive rods made accordingto the present invention. One can easily observe the two layers as theyspirally wrap along the length of the rod.

From the schematics of FIGS. 1-3 and the photographs of actual examplesshown in FIGS. 4-8, certain general principals and observations withrespect to preferred abrasive grits according to the present inventionwill become apparent. Typically, the grits will have at least oneinternal layer which is, and in cross-section exhibits, a continuousartifact, of at least 10 micrometers in length, typically at least 30micrometers, more typically at least 50 micrometers, often at least 70micrometers and in many instances 100 micrometers or more. The artifactmay be straight, or extend continuously through curves, etc. In general,material on opposite sides of the layer or layer artifact will be viewedto be continuous also, and generally contiguous with the layer or layerartifact. That is, there is generally no separation between the layerand materials adjoining it on opposite sides; and, the materials joiningthe layer on opposite sides generally themselves extend continuously forat least 10 micrometers, typically at least 30 micrometers, moretypically at least 50 micrometers, often at least 70 micrometers and inmany instances at least 100 micrometers. In some instances the layerartifact will be viewed to extend continuously at least 50%, preferablyat least 75%, of the distance across the greatest dimension of theabrasive grit viewable in the cross-section. When the layer is viewed asextending across the viewed cross-section, it may be characterized asintersecting an outer periphery of the abrasive grit at two, spaced,locations. It is also shown that systems having multiple internal layersare readily made, and identifiable using the techniques describedherein.

It is apparent that typically if a layer goes through folds, bends ornodes, generally layers immediately adjacent to it go through somewhatanalogous folds, bends or nodes. This results from the typical method ofpreparation, co-extrusion. This effect may not extend, completely,throughout the entire system when a great many layers are involved,however.

The use of double cross-sectioning, i.e., a first cross-section and anorthogonal cross-section, to characterize or evaluate a layer in severaldimensions is readily demonstrated and understood from FIGS. 3 and 6.

A variety of desirable features can be accommodated using the techniquesdescribed herein. For example, a relatively expensive component may beincluded in one or more of the co-extruded compositions, but not in all.The abrasive grit may be provided with certain advantages resulting fromthe component, without the need for use of quite as much component, byweight, in the overall composition from which the grits are formed. Thisis exemplified by Experiment 2. The zirconia introduced in one of thelayers of Example 2 results in a layer which is relatively hard and hasdesirable fragmenting characteristics, with respect to use in abrasives.Through the co-extrusion process described, the zirconia did not have tobe included throughout the grit, but rather a lower amount of zirconia,localized in specific layers, can provide an advantageous abrasive.

It is also foreseen that in some systems it may be desirable to havelayers with different properties, to achieve desired operating effects.These can be readily achieved with the techniques described.

Examples of Usable Sol-Gel Compositions

1. Dispersion-type Compositions

Among the types of compositions usable as "sol-gels" or "sols" in thetechniques described herein, are dispersion-type compositions. The terms"dispersion-type compositions" and variants thereof, are meant to referto compositions in which the alumina ceramic or alumina ceramicprecursor is in the form of a suspended solid. That is, the aluminaceramic precursor is not in solution. Dispersion-type compositions,usable in sol-gel techniques for preparing ceramics, are well known.Versions of them are discussed, for example, in the followingreferences, each of which is incorporated herein by reference: U.S. Pat.Nos. 4,881,951 (Wood et al.); 4,770,671 (Monroe et al.); 4,744,802(Schwabel); 4,574,003 (Gerk); 4,314,827 (Leitheiser et al.); 4,623,364(Cottringer et al.); 4,964,883 (Morris et al.); 5,201,916 (Berg et al.);5,728,184 (Monroe); 5,776,214 (Wood); 5,779,743 (Wood); 5,893,935(Wood); and U.S. application Ser. No. 08/781,557 (filed Jan. 9, 1997).

A. Alpha-alumina hydrate sols

A typical useful dispersion-type composition (or sol) comprises amixture of liquid medium and alpha alumina monohydrate (typicallyboehmite), although other hydrates may be used. The boehmite (or otherhydrate) can be prepared by any of various conventional techniques, orit can be acquired commercially. Suitable boehmite is commerciallyavailable, for example, under the trade designations "DISPERAL" fromCondea Chemie, GmbH, of Hamburg, Germany, and "DISPAL", "CATAPAL A","CATAPAL B", and "CATAPAL D" from Condea Vista Chemical Co. of Houston,Tex. Other commercially available boehmites which may be useful includethose available from LaRoche Industries of Atlanta, Ga., e.g., under thetrade designations "VERSAL 150", "VERSAL 250", "VERSAL 450", "VERSAL700", "VERSAL 850", and "VERSAL 900" (see, e.g., U.S. Pat. No. 5,728,184(Monroe), the disclosure of which was previously incorporated herein byreference). The commercial aluminum oxide monohydrates referred to aboveare in alpha form, are relatively pure (including relatively little, ifany, hydrate phases other than monohydrate), and have high surfaceareas.

Preferably, when boehmite is used in methods according to the presentinvention, the boehmite selected has an average ultimate crystallitesize of less than about 20 nanometers (more preferably, less than about12 nanometers); with "crystallite size" being defined by the longestdimension of a crystallite.

As the incorporated references indicate, a variety of liquid media,organic or non-organic, can be utilized as the liquid for thedispersion. Suitable liquids include water, alcohols (typically C₁ -C₆alcohols), hexane, and heptane. In general, water (most preferably,deionized water) is the preferred and most widely utilized liquidmedium, due primarily to convenience and cost. In some instances it maybe desirable to use tepid water. In still others warm or hot water maybe desirable.

Typically, when the alumina precursor is boehmite, the dispersion willcontain at least 10% by weight deionized water, more commonly betweenabout 20% and 80% by weight deionized water. Typical, preferred,dispersions comprise from about 2% to about 80% by weight alpha aluminumoxide monohydrate (typically boehmite), typically about 30% to 65%weight percent. The weight percent is based on a total of hydrate plusliquid carrier, without regard to adjuvants or additives. In someinstances the alumina precursor may be a recycled material from previousprocessing, as described in U.S. Pat. No. 4,314,827 (Leitheiser et al.).

A peptizing agent or dispersion aid may be used to produce a more stablesol or colloidal dispersion. Monoprotic acids which may be used as thepeptizing agent include acetic, hydrochloric, formic, and nitric acids.Nitric acid is preferred, especially with boehmite sols. Multiproticacids are normally to be avoided since they can rapidly gel thedispersion or sol, making it more difficult to handle or to mix inadditional components. Some commercial sources of boehmite contain anacid titer (e.g., acetic, formic, or nitric acid) to assist in forming astable dispersion.

The use of defoamers can be helpful in decreasing foaming or frothingwhich otherwise occurs during milling or stirring. Suitable defoamersinclude citric acid and its salts. A defoamer is typically used in anamount corresponding to about 1% by weight of the aluminum oxide (on atheoretical oxide basis) present in the dispersion.

Suitable methods for mixing the dispersion include ball milling,vibratory milling, and/or high shear mixing (colloid mills). High shearmixing is the preferred mixing method. Suitable mixers include pailmixers (available, for example, from Sears Roebuck & Company), sigmablade mixers (available for example, from Paul O. Abbe, Inc. of LittleFalls, N.J.) and high shear mixers (available, for example, from CharlesRoss & Son Co., Hauppauge, N.Y.). Other suitable mixers may be obtainedfrom Eirich Machines, Inc. of Gurnee, Ill.; Hosokawa-Bepex Corp. ofMinneapolis, Minn. (including a mixer available under the tradedesignation Schugi Flex-O-Mix, Model FX-160); and Littleford-Day, Inc.of Florence, Ky.

It is also possible that the mixing can be done within an extruder, ifdesired. This extruder can be a single screw or twin screw extruder.

B. Sols of alpha-alumina or alpha-alumina precursor (other thanhydrates)

Dispersions (or sols) of alpha-alumina particles or alpha-aluminaprecursor particles (other than hydrates) can also be used. In general,techniques including them are similar to those involving hydrates.

A preferred alpha alumina material is commercially available under thetrade designation "AKP-50" from Sumitomo Chemical of Japan. Varioustransitional alumina as suitable for use in preparing the secondpreferred alumina-based dispersion include chi alumina, gamma alumina,eta alumina, and mixtures thereof. A suitable transitional alumina whichincludes chi alumina is commercially available, for example, under thetrade designation "AA100W" from Alcan Corp. of Cleveland, Ohio.

It is preferred that the particulate alumina material, from which thedispersion is formed, comprise powdered material having a particle sizedistribution such that no more than about 0.5% by weight is greater thanabout 2 micrometers, and preferably such that no more than 5.0% byweight is greater than 1 micrometer in size (diameter or longestdimension). Preferably, the particle size is on the order of at leastabout 75% by weight smaller than about 0.7 micrometer, and, morepreferably, 99% by weight is less than about 0.7 micrometer. Suchparticulate material typically not only readily forms the dispersion butalso provides a useful precursor to the desired sintered product.Particle sizes within the preferred ranges can be obtained fromcommercially available materials, or can be prepared, for example, bycrushing or ball milling (wet or dry) an alumina source.

As with the hydrates discussed above, a variety of liquid media, organicor non-organic, can be utilized as the liquid for the dispersion.Suitable liquids include water, alcohols (typically C₁ -C₆ alcohols),hexane, and heptane. In general, water (most preferably, deionizedwater) is the preferred and most widely utilized liquid medium, dueprimarily to convenience and cost.

In general, the preferred ratio of liquid medium to powdered aluminawill be dependent upon the particle size distribution as it relates tothe surface area of the powdered material. If water is used, typicallyweight ratios within the range of about 1:6 (i.e., liquid medium topowdered raw material) to 15:1 will be chosen, although ratios outsideof this range may also be useful. It is typically preferred to avoid theuse of excess liquids in order to minimize the extent of subsequentdrying. It is, however, preferred to use a sufficient amount of liquidso the thoroughly mixed dispersion can be readily handled or moved, forexample, by pouring, siphoning, pumping, or extruding.

It is foreseen that if the alumina has relatively high surface area, forexample, about 200-300 m² /g (e.g., that commercially available underthe trade designation "AA100W" from Alcan), a weight ratio of water topowder of about 5:1 to 10:1 is preferred (about 6:1 to 9:1 mostpreferred). If, however, the alumina has a relatively low surface area,for example, less than about 20 m² /g (e.g., commercially availableunder the trade designation "A16" from Alcoa, Pittsburgh, Pa.), a weightratio of about 1:6 to 2:1 is preferred.

Preferably, the solids content of the dispersion is maximized, and thesolids (i.e., particles) are dispersed homogeneously therein.Preferably, the size of the pores in the material dried from thedispersion is minimized. Further, it is preferred that the distributionof pore sizes is as narrow as possible.

In general, the liquid medium, dispersed alumina and other optionaladditives are mixed until a homogenous slurry or stable dispersion isformed. This mixture, which is sometimes referred to herein as a "stableslip", is one in which, in general, the solids of the slurry do notappear by visual inspection to begin to separate or settle upon standingfor about 2 hours (due, it is believed, to the viscosity of the slurry).A stable dispersion can be obtained by thoroughly mixing the alumina,any dispersion aid, and any additional raw materials and additives intothe liquid medium, reducing the size of, and/or deagglomerating theparticles in the dispersion until the resulting dispersion ishomogeneous, and the individual alumina (powder) particles aresubstantially uniform in size and distribution. Suitable methods formixing include ball milling, vibratory milling, air stirrer, Coulesdissolver, attrition milling and/or high shear mixing (colloid mills).Pebble (e.g., ball, vibratory, attrition) milling techniques aregenerally most preferred because of their ability to readily reduce thesize of the alumina starting material.

Dispersions prepared as described in this section are typicallythixotropic. "Thixotropic", as used herein, is meant to describe aslurry that is viscous when under no stress, but has a low viscositywhen shear (e.g., mixing) is introduced. It generally comprises a chalkyor milky liquid which can be easily poured or stirred, but which issufficiently thick so that the solids do not settle within a two-hourperiod. Dispersions or slips prepared according to the methods describedin this section generally have a consistency of about that for latexpaint. Undesirable lumpy or heterogeneous mixtures tend to result frominadequate mixing.

Dispersion aids may be used to improve the consistency or stability ofthe dispersion or slurry. Dispersion aids tend to help prevent orminimize settling and improve the homogenous nature of the slurry byhelping to break down large agglomerates.

Preferred dispersion aids include strong acids (e.g., nitric acid) andbases (e.g., ammonium hydroxide), polyanionic polymers such ascarboxylate functional polymers, (e.g., polyacrylic acids, polyacrylicacid copolymers, and polyacrylic acid salts), and basic aluminum saltssuch as basic aluminum chlorides and basic aluminum nitrates. Suitablecarboxylate functional polymers are available, for example, under thetrade designations "JONCRYL" from Johnson Wax, Inc., of Racine, Wis.;"CARBOPOL" from the B.F. Goodrich Co. of Cleveland, Ohio; "NOECRYL" fromICI Resins US of Wilmington, Mass.; and "VINAC" from Air Products andChemicals, Inc., of Allentown, Pa.

The desired amount of dispersion aid is believed to depend on thesurface area of the particles to be dispersed. Generally, the preferredamount of dispersion aid increases as the surface area of particlesincreases.

In general, for a dispersion employing strong acids or bases asdispersion aids, sufficient dispersion aid is used to render a pH ofless than about 6 (preferably, about 2 to 3) or more than about 8(preferably, about 8 to 10), respectively.

The most preferred strong acid dispersant is typically nitric acid.Dispersions employing concentrated (70%) nitric acid as the dispersantpreferably contain about 2-15% by weight nitric acid, based upon totalsolids content of the dispersion. The stability of such dispersions maybe improved by heat treating the dispersion, for example, by autoclavingit.

Dispersions employing polymeric or basic aluminum salt material as thedispersant preferably contain about 0.1 to about 4% by weight of suchdispersant, based on the total solids content of the dispersion.

As with the dispersions of alpha alumina hydrates discussed in theprevious section, the use of defoamers can be helpful in decreasingfoaming or frothing which otherwise occurs during milling or stirring.Suitable defoamers include citric acid and its salts. A defoamer istypically used in an amount corresponding to about 1% by weight of thealuminum oxide (on a theoretical oxide basis) present in the dispersionor solution.

The dispersion may include other additives such as organic binders(e.g., polyethylene glycol, commercially available, for example, underthe trade designation "CARBOWAX" from Union Carbide of Akron, Ohio) andorganic solvent(s) (e.g., toluene and hexane). The amounts of thesematerials are selected to give a desired property (e.g., ease ofprocessing, improved drying of the solids, improved green strength, andreduced foaming).

2. Solutions of Aluminum Salts

Solution-based compositions or sols (not dispersions ofAlpha-alumina/alpha-alumina precursors or gels) can be prepared fromaluminum salts by techniques also known in the art. Typical preparationtechniques include dissolving an aluminum-based salt or complex inwater; or diluting or concentrating a solution comprising analuminum-based salt or complex. Preferably, the solution-basedcomposition comprises, in the range of about 5 to about 45 weightpercent, alpha alumina precursor. Preferably, the solution-basedcomposition comprises a soluble aluminum salt or other solublealuminum-based complex. More preferably, the solution-based compositioncomprises at least one of the following alpha alumina precursors: abasic aluminum carboxylate, a basic aluminum nitrate, and a partiallyhydrolyzed aluminum alkoxide.

Preferred solution-based compositions include those comprising basicaluminum salts with carboxylate or nitrate counterions or mixturesthereof Preferred aluminum carboxylates are represented by the generalformula, Al(OH)_(y) D_(3-y), wherein y can range from between about 1and about 2, preferably between about 1 and about 1.5, and D (thecarboxylate counterion) is typically an anion such as formate, acetate,propionate, oxalate, and combinations thereof, although others may beused. Aluminum carboxylates can be prepared by techniques known in theart including the methods described in U.S. Pat. No. 3,957,598 (thedisclosure of which is incorporated herein by reference), whereinaluminum metal is digested in a carboxylic acid solution and U.S. Pat.No. 4,798,814 (the disclosure of which is incorporated herein byreference), wherein aluminum metal is dissolved in a hot aqueoussolution comprising formic acid and acetic acid.

Preferred basic aluminum nitrates are represented by the generalformula, Al(OH)_(z) (NO₃)_(3-z) wherein z is in the range of about 0.5to about 2.5. The preparation of basic aluminum nitrates is known in theart and includes the methods taught in U.S. Pat. No. 3,340,205 andBritish Pat. No. 1,139,258 (the disclosures of which are incorporatedherein by reference), wherein aluminum metal is digested in a nitricacid solution. Basic aluminum nitrates may also be prepared according toU.S. Pat. No. 2,127,504 (the disclosure of which is incorporated hereinby reference), wherein aluminum nitrate is thermally decomposed.

3. Hybrid approaches

It is within the scope of the present invention to prepare abrasive gritprecursor from a dispersion prepared by providing dissolved aluminumsalts in a dispersion of alpha alumina and/or alpha alumina precursor,or by mixing a dispersion of alpha alumina and/or alpha aluminaprecursor with a solution-based composition. Other mixtures of thevarious types of materials discussed above can also be used.

Other Additives

The dispersion or solution optionally may include precursor of oxidemodifier (e.g., precursor to, or oxides of, aluminum, magnesium, cerium,zinc, cobalt, nickel, zirconium, hafnium, iron, silicon, manganese,chromium, yttrium, calcium, lithium, sodium, strontium, praseodymium,erbium, titanium, vanadium, tantalum, niobium, samarium, ytterbium,neodymium, lanthanum, gadolinium, dysprosium, and mixtures thereof) toenhance some desired property of the sintered abrasive particle or toincrease the effectiveness of a subsequent processing step (e.g., thesintering step). Such precursors are generally introduced in the form ofsalt (typically a metal salt material) soluble in the liquid carrier ofthe dispersion. Typically, the precursor is a water soluble metal salt.A preferred combination of modifiers is magnesium, neodymium, lanthanumand yttrium at levels of about 0.75%-2.5%, 0.75%-1.5%%, 0.75%-1.5%, and0.75%-1.5% by weight, respectively, on an oxide basis in the final firedabrasive.

For additional details regarding the inclusion of manganese oxide andprecursors thereof in the dispersion or solution, see U.S. Pat. No.5,690,707 (Larmie et al.), the disclosure of which is incorporatedherein by reference.

The dispersion or solution may contain a nucleating material to enhancethe transformation of the alpha alumina precursor to alpha alumina.Suitable nucleating materials include fine particles of alpha alumina,or fine particles or precursors of alpha ferric oxide, chromia,titanates, and any other material which will nucleate thetransformation, with alpha alumina and alpha ferric oxide being thepreferred materials. Nucleating materials are disclosed, for example, inU.S. Pat. Nos. 4,623,364 (Cottringer et al.), 4,744,802 (Schwabel),4,964,883 (Morris et al.), and 5,219,806 (Wood), the disclosures ofwhich are incorporated herein by reference.

If it is desired that the resulting sintered alpha alumina-based ceramicabrasive grit include zirconium oxide and/or cerium oxide, a preferredmethod for introducing zirconium oxide and/or cerium oxide is by addingzirconia particles and/or ceria particles to the dispersion or solution.These materials can be added to the dispersion or solution as a sol oras a fine powder. For additional details regarding such zirconium andceria additions, see: U.S. Pat. Nos. 5,551,963 (Larmie) and 5,429,647(Larmie), the disclosures of which are incorporated herein by reference.

The Step of Co-Extrusion

One preferred manner of preparing stratified or layered abrasive gritsaccording to the present invention is through a co-extrusion of two ormore "different" compositions. By the term "different" in this context,it is meant that the compositions extruded (i.e., being compared) differfrom one another in at least one manner. The manner of difference may,for example, be: the presence or absence of some nucleating material orseed material; a difference in amount and/or type of nucleating or seedmaterial; a presence or absence of some precursor of an oxide modifier;different amounts of, and/or different types of, precursor of an oxidemodifier; use of different aluminum oxide ceramic precursors; use of thesame ceramic oxide precursor but with different sized particles; thepresence or absence of some oxide additive, etc. From these examples itwill be apparent that the intent with respect to this use of the term"different" is that there be at least one difference between theco-extruded compositions; and, it is intended to accommodate anydifference or level of difference.

As mentioned, in some applications it may be desired to co-extrude twomaterials, which although prepared differently, may result inessentially the same microstructure and chemical structure.Additionally, advantages may be seen from co-extruding two identicalmaterials, although in the final product no difference would be observedbetween the two structures.

A variety of co-extrusion techniques can be used. For example, the two(or more) compositions can be simultaneously and continuouslyco-extruded into a layered form. The co-extrusion can be conducted toform two continuous layers in the extrusion, or more layers. Theextrusion can be continuous or intermittent, with respect to one or moreof the various compositions extruded. Examples of useable extrudersinclude ram extruders, single-barrel extruders, double-barrel extruders,twin screw extruders, and segmented screw extruders. Suitable extrudersare available, for example, from Loomis Products of Levitown, Pa.,Banpok Co. of Uniontown, Ohio and Hosokawa Bepex of Minneapolis, Minn.,which offers, for example, an extruder under the trade designationExtrud-O-Mix (model EM-6). The dispersion can be extruded in a form of arod, which can be deliquified and crushed, cut, or broken into smallersized rods or particles. The extruded dispersion can also be shreddedand graded. If the abrasive grit is shaped as a rod, it may have adiameter of 30 to 5000 microns, generally 100 to 500 microns, and anaspect ratio (i.e., length to width ratio) of at least 1, generally 1 to25, more preferably 2 to 8, and most preferably 2 to 4. Thecross-sectional area of the rod may be a circle, oval, star, cross,square, or any other shape. Additionally, the rod may be straight, ormay be twisted or curved.

FIGS. 9 and 10 are schematics of processes useable for the production ofthe abrasive grit according to certain embodiments of the invention.FIG. 9 shows first composition 31 and second composition 32, twoseparate and distinct dispersion streams, being fed into stratifyingmixer 34. Mixer 34 has a first section 35 and a second section 36. Astratifying mixer typically has static mixing elements fixed in aconduit. The elements divide, invert, and radially mix material receivedfrom the preceding element with a programmed precision and efficiency.Two inlet streams become four alternating streams after the firstelement, either after the second element, and so on. The cross sectionof the resulting extrudate or off-stream 39, when viewed in theextrusion direction, shows alternating layers of first composition 31and second composition 32.

Likewise, FIG. 10 shows first composition 41, second composition 42, andthird composition 43, three separate and distinct dispersion streams,being fed into stratifying mixer 44. Mixer 44 has a first section 45 anda second section 46. The cross section of the resulting extrudate oroff-stream 49, when viewed in the extrusion direction, shows alternatinglayers of composition 41, composition 42 and composition 43.

The co-extrusion or extrudate can be mixed, i.e., be passed through amixer, such as a stratified mixer, to generate still further layers ofany extruded materials. An example of this is provided hereinbelow, inconnection with the examples. More generally, microstratefying mixturesproduce controlled stratification in the extruded material, rather thanrandom flow, Standard mixing elements fixed in a conduit divide, invertand radially mix materials received from the preceding element with aprogrammed precession and efficiency. For example, two inlet streamsbecome four alternating streams after the first mixing element, eightafter the second element and so on. Thus, the number of strata increasesexponentially with the number of mixing elements. Microstratifiers,then, can be quite effective in generating a number of striations in theextruded product or extrudate, resulting from relatively few feedsthrough the extrusion dock.

FIG. 11 is a schematic of an example of a process which can be used toproduce the alumina abrasive grits of the present invention. Holdingtanks 91 and 101, respectively, contain sol or gel 92 and 102,respectively. In one embodiment, sol or gel 92 and 102 are differentfrom one another in some manner. Holding tanks 91 and 101 may have, forexample, holding capacities anywhere from 5 liters to 50,000 liters,depending on the desired output from the process. Sols or gels 92 and102 are pumped from holding tanks 91 and 101, respectively, by pumps 94and 104, respectively. These pumps 94 and 104 are most preferablyprogressive cavity pumps because of their ability to handle liquid, gelsand solids. Prior to being thoroughly mixed in pin mixers 98 and 108,gelling agent, stored in tank 96 and 106, can be added to the flow ofsols or gels 92 and 102, respectively, to increase the sol or gelviscosity. A typical gelling agent is, for example, nitric acid. Oncethe sols or gels are at a preferred viscosity, they can then be combinedinto one feed stream at 107 and are stratified in static mixer 99. Anextrudate or off-stream 100 from mixer 99 can then be dried andprocessed further as described below to produce alumina abrasive grits.

Follow-up Processing

In general, follow-up treatment of the co-extrusion or extrudate,whether mixed or not, can be conducted with standard techniques for usein sol processing to form abrasive grits. As indicated in suchreferences as U.S Pat. Nos. 4,314,827; 4,881,951; 4,770,671; and5,164,348, incorporated herein by reference, these techniques generallyinvolve the steps of drying and firing (sintering), in some instanceswith separate steps of calcining (also known as prefiring) and/orimpregnation. Before the material is fired or sintered it is converted,generally crushed, into particulate material. The term "converted" meansthat the nonsintered sintered or non-fired material is either cut,broken, crushed, or otherwise modified into the desired shaped ordesired particle size distribution. The material can be sized and gradedaccording to selected grades either before or after sintering.

Conventional crushing approaches which are useable include rollcrushing, ball milling, and hammer milling.

Air drying steps may be used to remove water (or other volatiles) fromthe extrusion. Drying can be accomplished, for example, in a forced airoven at a temperature in the range of about 50° C. to about 200° C.,preferably between about 100° C. and 150° C. Generally, drying isconducted until the dried gel contains 1 to 40%, preferably, 5 to 20% byweight, free-water.

The dried gel is typically calcined or pre-fired to remove any tracewater or solvent. During calcining, the dried gel is generally heated toa temperature in the range from about 400° C. to about 1000° C.,preferably about 400° to about 800° C. The dried gel is held within thistemperature range until the free water and preferably over 90 percent byweight of any bound volatiles are removed. If the dried gel contains amodifier precursor, the dried gel is preferably calcined for a period oftime sufficient to achieve essentially complete conversion of themodifier precursor to metal oxide.

Optionally, the dried or calcined material may be impregnated withmodifier. General methods of impregnating particles derived from aluminahydrate dispersions are described, for example, in U.S. Pat. No.5,164,348 (Wood), the disclosure of which is incorporated herein byreference.

In general, the calcined or dried material is porous. For example,calcined material generally has pores about 4 to 10 nanometers indiameter extending therein from an outer surface. Impregnation of thepores with an impregnation composition comprising appropriate modifierprecursor and a liquid medium provides for increases in density and canimprove toughness of the sintered alpha alumina-based particle. Themodifier for impregnation (i.e., the impregnate) generally is aprecursor of a metal oxide provided in the form of one or more salts ofa metal (e.g., a nitrate or acetate salt). It is also within the scopeof this invention to impregnate with an aluminum salt. The metal saltmaterial is dissolved in a liquid medium, and the resulting solution isthen mixed with the porous base particle material. The impregnationprocess is thought to occur through capillary action. The capillaryaction can be improved by subjecting the porous material to vacuumtreatment before or during the impregnation step. U.S. application Ser.No. 08/781,557 (filed Jan. 9, 1997)(Wood) discloses subjecting calcinedmaterial to a vacuum just after impregnation. During the impregnation oflarge grits, e.g., greater than 400 micrometers, the calcined materialcracks and splits due to the change in pressure, so as to provide sharpedges and points on the resulting abrasive particle. Such a techniquecan be applied with abrasive grits or particles prepared according tothe techniques disclosed herein.

The liquid media used for the impregnating composition is preferablywater (including deionized water) and/or an organic solvent (preferablya non-polar solvent). If the particulate material is calcined prior tothe impregnation step, water is the preferred liquid media for theimpregnation composition. If the particulate material is not calcinedprior to the impregnation step, the liquid media preferred is one thatwill not dissolve or soften the particulate material.

The concentration of the salt in the liquid medium is typically in therange from about 5% to about 40% dissolved solids, on an oxide basis. Ingeneral, there should be at least 50 ml of solution added to achieveimpregnation of 100 grams of porous base particle material, preferably,at least about 60 ml of solution to 100 grams of base particles and mostpreferably at least 70 ml of solution to 100 grams of the baseparticles. Examples of preferred impregnating solutions comprise saltsof magnesium, neodymium, lanthanum, and yttrium.

In some instances, more than one impregnation step may be utilized. Thesame impregnation composition may be applied in repeated treatments, orsubsequent impregnation compositions may contain differentconcentrations of the same salts, different salts, or differentcombinations of salts.

During heat treatment of the impregnated material to form the sintered,ceramic, alpha alumina-abrasive grits, the impregnate (or modifier) mayreact with alumina to form a reaction product. For example, the oxidesof cobalt, nickel, zinc, and magnesium typically react with alumina toform a spinal structure. Yttria typically reacts with alumina to form3Y₂ O₃ ·5Al₂ O₃, which has the garnet crystal structure. Praseodymium,samarium, ytterbium, neodymium, lanthanum, gadolinium, cerium,dysprosium, erbium, and mixtures of two or more of these rare earthmetals typically react with alumina to form garnet, beta alumina, orphases exhibiting a perovskite structure. Certain rare earth oxides anddivalent metal oxides react with alumina to form a rare earth aluminaterepresented by the formula LnMAl₁₁ O₁₉, wherein Ln is a trivalent metalion such as La, Nd, Ce, Pr, Sm, Gd, or Eu, and M is a divalent metalcation such as Mg, Mn, Ni, Zn, Fe, or Co. Such rare earth aluminatestypically have a hexagonal crystal structure that is sometimes referredto as a magnetoplumbite crystal structure. Such rare earth aluminatesgenerally have exceptional properties in an abrasive grit and ifpresent, are typically within the abrasive particle as a whisker(s) orplatelet(s). Such whiskers or platelets typically have a length of about0.5 micrometer to about 1 micrometer, and a thickness of about 0.5micrometer or less. It is believed that the whiskers or plateletsinhibit crack propagation. These whiskers or platelets are more likelyto occur in the absence of a nucleating agent.

It would not be outside the scope of this patent to incorporate a hardparticulate material such as a carbide, silicide, oxide, boride,nitride, oxycarbide, oxynitride, carbonitride or mixtures thereof intothe layers of the α-alumina based precursor or precursors.

In one aspect of the invention, the abrasive grit consists essentiallyof metal oxides, a-alumina with other metal oxides. This abrasive gritwill then be essentially free of non-oxides, i.e., the abrasive gritwith less than about 0.1% non-oxides. These non-oxides are typicallycarbides, silicides, borides, nitrides, oxycarbides, oxynitrides,carbonitrides or mixtures thereof.

In another aspect of the invention, the abrasive grit can comprise amixture of metal oxides with non-oxides. These non-oxides are typicallycarbides, suicides, borides, nitrides, oxycarbides, oxynitrides,carbonitrides or mixtures thereof.

Metal Oxide Surface Coatings (Optional)

It is within the scope of the present invention to provide aluminaabrasive grits, as described above, which have the outer surface of theabrasive grit coated with a metal oxide. The metal oxide coating can becontinuous or discontinuous, and be fairly dense with no porosity, or beporous. The thickness of the metal oxide coating is preferably in therange of about 0.05 to 20 micrometers, more preferably about 0.1 to 10micrometers. Suitable metal oxides include, for example, oxide oftitanium, zirconium, aluminum, chromium, vanadium, tantalum, hafnium,niobium, and combinations thereof For purposes of the presentapplication, the term "metal oxide" is also intended to refer to siliconoxide. Various metal oxide coatings useful for this invention aredescribed below, although the scope of this invention is not limited tothese embodiments.

A coating of inorganic metal oxide particulates on the base particleprovides a (sintered) abrasive particle having an increased surface areafor improved adhesion to the bond system. Preferably, the particulatemetal oxide coating on the sintered abrasive particle (or abrasive core)is relatively porous. Also, preferably, at least 70% (more preferably,at least 80%) of the surface area of the sintered alpha alumina-basedparticle (or core) is covered with the inorganic metal oxide particulatecoating, although greater than 90% coverage may be obtained. Withrespect to the amount of coverage, reference is made to the amount ofexposed sintered particle (core) surface in the resulting coatedabrasive particle. Thus, "coverage of at least 70%" means that no morethan about 30% of the total area of the underlying sintered baseparticle surface is exposed (i.e., not covered with particulates). Theamount of coverage in this context is not meant to refer to the nature(e.g., porosity or density) of the particulate coating. The coating canbe continuous or discontinuous.

The density of the metal oxide coating is typically less than 90%(preferably less than 80%) of theoretical. Most preferably, the coatinghas a density of at least 40%, but less than 70% of theoretical. This isnot meant, however, to imply that the coating is discontinuous, butrather to reflect that pores extend therethrough. Further, the densityvalue given is meant to refer to the average density of the coating, notthe density of the individual fused particulates that make up thecoating (i.e., the coating comprises dense particulates packed togetherwith some open space therebetween).

During sintering, the inorganic metal oxide particulates in the coatingtypically sinter to one another resulting in a coating having goodstructural integrity. The resulting coating may contain more than onelayer of inorganic metal oxide particulates. Typically, there are 2 to30 layers, more typically, 3 to 20 layers of particulates. Preferably,at least 5 to 15 layers of inorganic metal oxide particulates areprovided, stacked on one another.

The inorganic metal oxide particulates can comprise, for example,transitional alumina, alpha alumina, hydrated aluminas, yttria,magnesia, rare earth metal oxides, zinc oxide, iron oxide, silicates,chromium oxide, titanium oxide, nickel oxide, yttria, alumina, garnet,hexagonal rare earth aluminate, alumina-zirconia, zirconium oxide,alumina oxynitride, silicon aluminum oxynitride, silicon aluminumoxycarbide, and combinations thereof.

U.S. Pat. No. 5,011,508 (Wald et al.), the disclosure of which isincorporated herein by reference, describes autogenously bonding fineinorganic metal oxide (e.g., alumina) particulates to the surface of abase particle via mechanical impingement and then sintering to providean abrasive particle having a particulate metal oxide coating.

A preferred metal oxide particulate surface coating is described in U.S.Pat. No. 5,213,591 (Celikkaya et al.), the disclosure of which isincorporated herein by reference, wherein an alpha alumina-based ceramicabrasive grit comprising an alpha alumina-based core having a coating ofinorganic metal oxide particulates autogenously bonded thereto isdescribed.

Other methods for providing other treatments and coatings of theabrasive grit known in the abrasive art (e.g., oxide coatings other thandescribed above) may be useful in the preparation of abrasive grits orparticles for use in the method according to the present invention.Examples of other metal oxide coatings are disclosed in U.S. Pat. No.5,474,583 (Celikkaya). Examples of still other coatings, e.g., boride,nitride and carbide are disclosed in U.S. Pat. Nos. 5,611,828(Celikkaya); 5,628,806 (Celikkaya et al.) and 5,641,330 (Celikkaya etal.). These latter coatings are typically applied to the grits aftersintering or firing.

Sintering

As indicated above, the non-fired (or non-sintered) base particles ortreated (e.g., impregnated, tumbled, and/or coated) base particles areprecursors to ceramic abrasive grits.

The sintering or firing of the precursor abrasive grit can beaccomplished through a variety of conventional processes. Typically,sintering is conducted at a temperature in the range from about 1200° C.to about 1650° C. Sintering generally can be accomplished within a timeperiod of a few seconds to about 120 minutes, but generally it is donewithin 3 to 30 minutes. Sintering of various types of base particles isdescribed, in general, in U.S. Pat. No. 4,314,827 (Leitheiser et al.),the disclosure of which is incorporated herein by reference. Anothertype of kiln useful for the sintering of the base particles, isdescribed, for example, in U.S. Pat. 5,489,204, (Conwell et al.) thedisclosure of which is incorporated herein by reference. The techniquesof sintering applied therein may be applied to treated base particles asdescribed herein. It is also within the scope of this invention tosinter in an inert or reducing atmosphere.

Abrasive Products

Abrasive grit according to the present invention and/or made accordingto the method of the present invention can be used in conventionalabrasive products, such as coated abrasive products, bonded abrasiveproducts (including grinding wheels, cutoff wheels, and honing stones),nonwoven abrasive products, and abrasive brushes. Typically, theabrasive products (i.e., abrasive articles) will include a binder andabrasive grit, at least a portion of which is abrasive grit madeaccording to the present invention and/or made according to the methodof the present invention secured within the abrasive product by thebinder. Methods of making such abrasive products are well known.Furthermore, abrasive grit made according to the present inventionand/or made according to the method of the present invention, can beused in abrasive applications that utilize slurries or abradingcompounds (e.g., polishing compounds).

Coated abrasive products generally include a backing, abrasive grit, andat least one binder to hold the abrasive grit on the backing. FIG. 12shows coated abrasive product 200 having backing 202 with abrasivecoating 203. Abrasive coating 203 comprises a plurality of abrasivegrits 204 embedded in make coat 205 and covered by make coat 206. Thebacking can be any suitable material, including cloth, polymeric film,fiber, nonwoven webs, paper, foams, sponges, combinations thereof, andtreated versions thereof The binder can be any suitable binder,including an inorganic or organic binder. The abrasive grit can bepresent in one layer or in two layers of the coated abrasive product.Preferred methods of making coated abrasive products are described, forexample, in U.S. Pat. Nos. 4,734,104 (Broberg); 5,316,812 (Stout etal.); 5,573,619 (Benedict et al.); and, 4,737,163 (Larkey), thedisclosures of which are incorporated herein by reference.

The abrasive grits of the present invention can also be incorporatedinto structured abrasive products. Such abrasive products generallycomprise a plurality of composites including binder and abrasive grits.The composites can be precisely shaped. Further information regardingsuch structures is found in: U.S. Pat. Nos. 5,152,917 (Pieper et al.)and 5,435,816 (Spurgeon et al.). The disclosures of the '917 and '816patents are incorporated herein by reference.

The abrasive product can have an attachment construction on its backsurface to secure the coated abrasive product to a support pad or backuppad. Such attachment constructions can be, for example, a pressuresensitive adhesive or one member of a hook and loop attachment such asdisclosed, for example, in U.S. Pat. No. 5,505,747 (Chesley et al.). Theback side of the coated abrasive product may optionally contain a slipresistant or frictional coating. Examples of such coatings include aninorganic particulate material (e.g., calcium carbonate or quartz)dispersed in an adhesive.

FIG. 13 shows bonded abrasive wheel 210 comprising abrasive grit 214 andbinder 215. Bonded abrasive products typically include a shaped mass ofabrasive grit held together by an organic, metallic, or vitrifiedbinder. Such a shaped mass can be, for example, in the form of a wheel,such as a grinding wheel or a cutoff wheel. It can also be in the form,for example, of a honing stone or other conventional bonded abrasiveshape. It is preferably in the form of a grinding wheel. For furtherdetails regarding bonded abrasive products, see, for example, U.S. Pat.No. 4,997,461 (Markhoff-Matheny et al.), the disclosure of which isincorporated herein by reference.

The vitreous binder may be fired at a temperature below 1200° C.,sometimes below 1100° C., and sometimes even below 1000° C. The vitreousbinder may comprise a frit vitreous binder.

Nonwoven abrasive products typically include an open porous loftypolymer filament structure having abrasive grit bonded thereto anddistributed throughout the structure and adherently bonded therein by anorganic binder. FIG. 14 shows nonwoven abrasive article 220 comprisingfilaments 222 with abrasive grits 224 and binder 225. Examples offilaments include polyester fibers, polyamide fibers, and polyaramidfibers. For further details regarding nonwoven abrasive products, see,for example, U.S. Pat. No. 2,958,593 (Hoover et al.) and PCT PublicationNo. WO 97/07937, the disclosures of which are incorporated herein byreference.

The abrasive grits of the present invention may also be used in abrasivebrushes and elements. Many examples of molded brushes are disclosed inPCT Publication No. WO 96/33638 and U.S. Pat. No. 5,679,067 (Johnson etal.), the disclosures of which are incorporated herein by reference.

Suitable organic binders for the abrasive products include thermosettingorganic polymers. Examples of suitable thermosetting organic polymersinclude phenolic resins, urea-formaldehyde resins, melamine-formaldehyderesins, urethane resins, acrylate resins, polyester resins, aminoplastresins having pendant αβ-unsaturated carbonyl groups, epoxy resins, andcombinations thereof. The binder and/or abrasive product can alsoinclude additives such as fibers, lubricants, wetting agents,thixotropic materials, surfactants, pigments, dyes, antistatic agents(e.g., carbon black, vanadium oxide, graphite, etc.), coupling agents(e.g., silanes, titanates, zircoaluminates, etc.), plasticizers,suspending agents, and the like. The amounts of these optional additivesare selected to provide the desired properties. The coupling agents canimprove adhesion to the abrasive grit and/or the filler. In some systemsthe coupling agents can be used to modify viscosity and/or to improvemixing.

The binder can also contain filler materials or grinding aids, typicallyin the form of a particulate material. Typically, the particulatematerials are inorganic materials. Examples of particulate materialsthat act as fillers include metal carbonates, silica, silicates, metalsulfates, and metal oxides. Examples of particulate materials that actas grinding aids include: halide salts such as sodium chloride,potassium chloride, sodium cryolite, and potassium tetrafluoroborate;metals such as tin, lead, bismuth, cobalt, antimony, iron, and titanium;organic halides such as polyvinyl chloride and tetrachloronaphthalene;sulfur and sulfur compounds; and graphite. A grinding aid is a materialthat has a significant effect on the chemical and physical processes ofabrading, which results in improved performance. In a coated abrasiveproduct, a grinding aid is typically used in the supersize coat appliedover the surface of the abrasive grit, although it can also be added tothe size coat. Typically, if desired, a grinding aid is used in anamount of about 50-300 g/m² (preferably, about 80-160 g/m²) of coatedabrasive product.

The abrasive products can contain 100% abrasive grit made according tothe present invention and/or made according to the method of the presentinvention or they can contain a blend of such abrasive grit withconventional abrasive grit and/or diluent particles. However, at leastabout 15% by weight, and preferably about 50-100% by weight, of theabrasive grit in the abrasive products should be abrasive grit havinglayered structures according to the present invention and/or madeaccording to the methods of the present invention. Examples of suitableconventional abrasive grit include diamond, cubic boron nitride, fusedaluminum oxide, silicon carbide, garnet, fused alumina zirconia, andother sol-gel-derived abrasive grit. Examples of suitable diluentparticles include marble, gypsum, flint, silica, iron oxide, aluminumsilicate, glass, metal oxide bubbles, hollow clay spheres, porous claypellets, solid or hollow glass spheres, expanded siliceous materials,hollow or solid resin spheres, and diluent agglomerates. Abrasive gritaccording to the present invention and/or made according to the methodof the present invention can also be combined in or with abrasiveagglomerates. Example of abrasive agglomerates are described in U.S.Pat. Nos. 4,311,489 (Kressner), 4,652,275 (Bloecher et al.), and4,799,939 (Bloecher et al.), the disclosures of which are incorporatedherein by reference.

The following non-limiting examples will further illustrate theinvention.

EXAMPLES

Sol I

Sol I was prepared by mixing 205 grams of boehmite (obtained under thetrade designation "DISPERAL" from Condea Chemie of Hamburg, Germany)into 360 grams of acidified water (prepared by mixing 10 grams ofconcentrated (70%) nitric acid with 350 grams of deionized water) in ablender (obtained from Waring Products Division, Dynamics Corp. ofAmerica, New Hartford, Conn.) for about one minute.

Sol II

Sol II was prepared as described for Sol I, except that 195 grams ofboehmite was used and 33 grams of zirconyl acetate (22% solidscalculated as ZrO₂ ; obtained from Magnesium Elektron, Inc. ofFlemington, N.J.) was added to the sol.

Sol III

Sol III was prepared as described for Sol I, except 30 grams of ironoxide aqueous dispersion (about 90 to 95% lepidicrocite; acicularparticles with an average particle size of about 0.05 to 0.1 micrometer,a length to diameter or width ratio of about 4:1 to 6:1, and a surfacearea of about 115.3 m² /g) having 5.1% iron oxide, calculated on atheoretical oxide basis as Fe₂ O₃, were added to the acidified waterprior to adding the boehmite.

Sol IV

Sol IV was prepared as described for Sol I, except 77 grams of a 20%colloidal zirconium acetate solution (obtained from Nyacol ProductsInc., Ashland, Mass.) were also added to the sol.

Sol V

Sol V was prepared as described for Sol I, except 53 grams of iron oxideaqueous dispersion (about 90 to 95% lepidicrocite; acicular particleswith an average particle size of about 0.05 to 0.1 micrometer, a lengthto diameter or width ratio of about 4:1 to 6:1, and a surface area ofabout 115.3 m² /g), having 2.9% iron oxide calculated on a theoreticaloxide basis as Fe₂ O₃ were added to the acidified water prior to addingthe boehmite,

Sol VI

Sol VI was prepared as described for Sol V, except 15 grams of a basiccolloidal silica sol (obtained from Nyacol Products Inc. under the tradedesignation "Nyacol 215") were added to the sol (i.e., to Sol V).

Sol VII

Sol VII was prepared as described for Sol I, except 15 grams of acolloidal ceria acetate (obtained from Nyacol Products Inc.) were addedto the sol (i.e., to Sol I).

Example 1 and Comparative Examples A and B

For Example 1, one chamber of each of four 50 ml dual chamber cartridges(obtained from Conprotec, Inc., Salem, N.H. under the trade designation"MIXPAC") were filled with Sol I. The remaining chambers were eachfilled with Sol II. For Comparative Example A, both chambers of each offour 50 ml dual chamber cartridges were filled with Sol I. ForComparative Example B, both chambers of each of four 50 ml dual chambercartridges were filled with Sol II.

Each cartridge was capped, burped of air, and allowed to stand for threedays. The twelve cartridges were placed in an oven at about 107° C.(225° F.) for two hours, and then cooled to room temperature.

The resulting gels were extruded from the respective cartridges intoglass trays. Thus, each dual chamber cartridge was used to conduct aco-extrusion. More specifically, the gels were extruded through a staticmixer nozzle (available under the trade designation "SCOTCH-WELD EPXMIXER NOZZLE" from the 3M, St. Paul, Minn.), having a tapered tip andten mixing elements, to form rods that were approximately one millimeterin diameter. (The mixer nozzle had 20 mixing elements but was cut inhalf so only 10 mixing elements were used.) The rods were dried byplacing them in an oven at about 107° C. (225° F.) for about one hour.

The dried rods were calcined for about 5 minutes at 650° C. in astainless steel rotary kiln (dimensions 1.2 m long, 15 cm diameter, 0.3m hot zone, tube inclined 2.4°, and rotating at 20 RPM), and thencrushed to shorter lengths using a pulverizer (type U.A., manufacturedby Braun Corp., Los Angeles, Calif.).

The crushed rods were impregnated with a rare earth nitrate solution ata ratio of 7 parts rare earth nitrate solution to 10 parts crushed rodsby weight. The rare earth nitrate solution was prepared by mixing alanthanum, neodymium, and yttrium nitrate solution (20.5% La(NO₃)₃ ·6H₂O), 20.1% Nd(NO₃)₃ ·6H₂ O, and 26.1% Y(NO₃)₃ ·6H20; available fromMolycorp of Lourviers, Colo.) with a sufficient amount of magnesiumnitrate solution (11% Mg(NO₃)₃ ·6H₂ O; available from MallinckrodtChemical of Paris, Ky.) and cobalt nitrate solution (15% Co(NO₃)₂ ·6H₂O; available from Hall Chemical of Wickliffe, Ohio) to provide asolution containing about 5.8 La(NO₃)₃ ·6H₂ O, 5.8% Nd(NO₃)₃ ·6H₂ O,about 7.1% Y(NO₃)₃ ·6H₂ O, about 14.4% Mg(NO₃)₂ ·6H₂ O, about 0.4%Co(NO₃)₂ ·6H₂ O, and the balance deionized water.

The impregnated rods were dried, calcined at 650° C. in the stainlesssteel rotary kiln, and sintered for about 5 minutes at 1410° C. in arotary kiln (dimensions 1.32 m long, 8.9 cm inner diameter, 31 cm hotzone) to provide sintered material.

The density of the sintered Example 1 and Comparative Examples A and Bmaterials, as measured with a He pycnometer (Micromeritos AccuPyc 1440;Micromeritics Instrument Corp. Norcross, Ga.), were 3.95 g/cm³, 3.97g/cm³, 3.91 g/cm³, respectively.

The hardness of Example 1 and Comparative Examples A and B material weremeasured on cross-sections polished to 1 micrometer. The microhardnesstester was obtained under the trade designation "MITUTOYO MVK-VL" fromMitutoyo Corp. of Tokyo, Japan. The measurement load was 500 grams. Theaverage hardness of Example 1 and Comparative Examples A and B material(5 independent readings per sample (i.e., 5 different individualparticles)) were 18.8 GPa, 18.9 GPa, and 18.9 GPa, respectively.

The sintered (rod) materials were broken to short lengths using aporcelain mortar and pestle. The length of the rods were approximately 3to 5 times the rod width or/diameter. These broken rods were screenedthrough a 25, 30, 35, and 40 mesh screen stack (USA Std. TestingSieves). The rods retained on the 30 and 35 mesh screens were blended ata weight of 5.4 grams of -30+35 mesh material and 12.6 grams of -25+30mesh material. This mixture, totaling 18 grams, was blended with 18grams of ANSI grade 24 brown fused alumina (obtained from WashingtonMills of North Grafton, Mass. and crushed and screened to the selectedgrade). These mineral blends were incorporated into coated abrasivediscs (three discs of each lot, about 12 grams of mineral per disc)using conventional techniques, including electrostatic coating of theabrasive grit. The resins used to make the discs was a CaCO₃ make,cryolite size and KBF₄ supersize.

The coated abrasive discs were mounted on a beveled aluminum back-uppad, and used to grind the face of a 1.25 cm by 18 cm 304 stainlesssteel workpiece. The disk was driven at 5,500 rpm while the portion ofthe disc overlaying the beveled edge of the back-up pad contacted theworkpiece at about a 6 kg load. Ten workpieces were ground per disc.Each disc was ground for ten minutes in one minute intervals using ten304 stainless steel workpieces (i.e., one minute per workpiece). Theaverage total cut for the Example 1 and Comparatives A and B coatedabrasive discs were 135.1 grams, 111.2 grams, and 129.6 grams,respectively.

This example showed grinding performance improvement of the co-extrudedExample 1 over the respective individual components (ComparativeExamples A and B). It also demonstrated a zirconium could beincorporated using co-extrusion without significant migration into otherphases. Thus, zirconia introduction could be efficiently achieved.

Example 2 and Comparative Examples C and D

Example 2 and Comparative Examples C and D were prepared as describedfor Example 1 and Comparative Examples A and B, respectively, except asfollows. For Example 2, Sols I and III were used in place of Sols I andII. For Comparative Example D, Sol III was used in place of Sol II. Eachcapped and burped cartridge was allowed to stand for 7 days rather than3 days. The extruded rods were dried in an oven at about 93° C. (200°F.) for about 2 hours, calcined at about 600° C., and sintered at about1440° C. in the rotary kiln.

The densities of the Example 2 and Comparative Examples C and D sinteredmaterials, as measured with the helium pycnometer, were 3.80 g/cm³ 3.82g/cm³, and 4.01 g/cm³, respectively.

The Comparative Examples C and D and Example 2 sintered materials, weresintered again in a box kiln (obtained under the trade designation"RAPID TEMP FURNACE" from C-M, Inc., Bloomfield, N.J.) at 1400° C. for10 minutes. The densities of the "twice-sintered" Example 2 andComparative Examples C and D materials, as measured with the heliumpycnometer, were 3.86 g/cm³, 3.85 g/cm³ and 4.01 g/cm³, respectively.

The "twice-sintered" (rod) materials were broken, screened, andincorporated into coated abrasive discs, and tested as described forExample 1 and Comparative Examples A and B. The average total cuts forthe Example 2 and Comparative Examples C and D coated abrasive discswere 102.9 grams, 105.3 grams, and 91.4 grams, respectively.

From this example, it could be seen that an iron oxide nucleating agentcould be incorporated into one phase of co-extruded phases withoutsignificant migration into the other phase. Thus, internal layeringaffects with different compositions one comprising iron oxide nucleatingmaterial, can be readily achieved.

Example 3 and Comparative Examples E and F

Example 3 and Comparative Examples E and F were prepared as describedfor Example 2 and Comparative Examples C and D, respectively, except asfollows. The capped and burped cartridges were first under vacuum andthen were allowed to stand 48 hours in air.

The gels were extruded into Pyrex trays through a 10 element staticmixer non-tapered tip. The mixer was prepared by removing the taperedtip from a Scotch-Weld EPX mixer nozzle. The extruded material was driedin an oven at about 93° C. (200° F.). The dried material for eachexample was crushed into random shapes using a mortar and pestle, andscreened to retain the -20+60 mesh (USA Std. Testing Sieves) material.Each screened material was calcined in the stainless steel rotary kilnat 650° C., impregnated, dried, calcined at 650° C., and sintered in arapid temp. kiln for 30 minutes at 1430° C.

The density of the sintered Example 3 and Comparative Examples E and Fabrasive grit materials, as measured using the helium pycnometer, were3.96 g/cm³ 3.89 g/cm³, and 4.01 g/cm³, respectively. The averagemicrohardness of the Example 3 abrasive grit material was 20.3 GPa inthe regions derived from Sol I, and 16.6 GPa in the regions derived fromSol III. The average microhardness of the Comparative Examples E and Fabrasive grit materials were 18.3 GPa and 21.3 GPa, respectively.

Coated abrasive discs were prepared as described in Example 1 andComparative Examples A and B and ground for ten minutes in two minuteintervals on 304 stainless steel. The coated abrasive disc was attachedto a 16.5 cm diameter, 1.57 mm thick hard, phenolic backup pad which wasin turn mounted onto a 15.2 cm diameter steel flange. The mounted discwas rotated counterclockwise at 3550 rpm. The 1.8 mm peripheral edge ofa 25 cm diameter 304 stainless steel disc (workpiece) deployed 7° from aposition normal to the abrasive disc under a load of about 4 kg. Theworkpiece was weighed at the start of the test and at 2 minute intervalsto determine the amount of stainless steel removed (i.e., abraded). Theaverage total cut for the Example 3 and Comparative Examples E and Fcoated abrasive articles was 165.2 grams, 155.8 grams, 148.8 grams,respectively. This example shows a performance improved of a coatedextrusion composition over the respective individual components (i.e.,Comparative Examples E and F).

Examples 4 and 5, Illustrative Example I, and Comparative Example G

Examples 4 and 5, and Illustrative Example 1 were prepared as describedfor Example 2, except the filled cartridges were placed under vacuum tode-air the sols. For Example 4, the mixer tip was cut to 6 cm; forExample 5 to 9 cm; and for Illustrative Example I, to 12 cm. ForExamples 4 and 5 and Illustrative Example I, the static mixers contained10, 15, and 20 mixing elements, respectively.

More specifically, Example 4 was extruded through a 6 cm static mixer;Example 5 through a 9 cm static mixer; and Illustrative Example I,through a 12 cm static mixer.

Comparative Example G was prepared by gelling Sol I in a glass tray(i.e., there was no extrusion step) and then further processing it asdescribed for Examples 4, 5, and Illustrative Example I. Examples 4 and5, Illustrative Example I, and Comparative Example G were allowed to dryat 93° C. overnight in a forced air oven.

The Examples 4 and 5, Illustrative Example I, and Comparative Example Gdried materials were each calcined at 650° C., crushed, and screened toretain -20+60 mesh (USA Standard Testing Sieves) material. Each of thescreened lots was soaked in the rare earth oxide solution under vacuumand then filtered through a Buchner funnel to recover the impregnatedmaterial. After drying, the impregnated materials were each calcined at650° C. in a prefire kiln, and then each sintered for 30 minutes usingthe box kiln ("RAPID TEMP") at 1430° C. (This impregnation step was ofthe type used in Example 1).

The Examples 4 and 5 calcined and sintered abrasive grit material wereobserved via light microscopy at 600× to each have distinct laminarmicrostructures composed of "nucleated" and "non-nucleated" regions. Thelaminate were much thinner and less distinct in Example 5 than inExample 4. Illustrative Example I appeared to be thoroughly mixed withonly "nucleated" phase observed.

The average microhardness of the "nucleated" portions of the sinteredExample 4 and 5, and Illustrative Example I materials were 19.5 GPa,20.1 GPa, and 19.9 GPa, respectively. The average microhardness of the"non-nucleated" portions of the sintered Example 4 and 5 and ComparativeExample G materials were 15.8 GPa, 16.4 GPa, and 18.2 GPa, respectively.

The average fracture toughness of the sintered Example 4 and 5,Illustrative Example I, and Comparative Example G materials were 3.0MPa·m^(1/2), 2.8 MPa·m^(1/2), 2.7 MPam·m^(1/2), and 2.5 MPam·m^(1/2),respectively. The fracture toughness was calculated by measuring thecrack lengths extending from the appeases from the Vikers indents madeusing a 1000 g load with a MITUTAYO MVK-VL hardness tester. Fracturetoughness (K_(1c)) was calculated according to the equation:(K_(1c))=FN/[(πc)^(3/2) tan b] wherein b=68°, π=pi (3.14159), F=Newtonsof Force on the indentor; c=1/2 crack length in meters. The density ofthe sintered Example 4 and 5, Illustrative Example I, and ComparativeExample G materials were 3.92 g/cm³, 3.94 g/cm³, 3.99 g/cm³, and 3.87g/cm³, respectively.

These examples show that the number of elements in the static mixer caninfluence the thickness of the layers.

Although not wanting to be bound by theory, it is believed that theimproved fracture toughness may be due to the increased laminarcharacter of the Example 4 and 5 materials. The improved fractureresistance due to the presence of a more porous (non-nucleated) laminarcould be readily observed via scanning electron microscopy whenexamining the cracks measured to obtain fracture toughness values.Cracks were observed to terminate within the porous laminae or turn andpropagate along the border between the seeded and non-seeded laminae.

Example 6 and Comparative Examples H and I

Example 6 and Comparative Examples H and I were prepared as describedfor Example 1 and Comparative Examples A and B, respectively, except asfollows. For extrusion a 6 cm static mixer length was used. For Example6, Sols I and IV were used in place of Sols I and II. For ComparativeExample I Sol IV was used in place of Sol II for Comparative H, Sol Iwas used.

The density of the Example 6 and Comparative Example H and I abrasivegrit materials were 3.97 g/cm³, 3.91 g/cm³ , and 4.00 g/cm³ ,respectively.

The average microhardness of the Example 6 and Comparative Example H andI abrasive grit materials were 19.4 GPa, 18.6 GPa, and 18.6 GPa,respectively. The average fracture toughness of the Example 6 andComparative Example H and I abrasive grit materials were 3.0 MPa·^(1/2),3.3 MPa·m^(1/2), and 3.3 MPa·m^(1/2), respectively.

Example 6, Comparative Example H, and Comparative Example I abrasivegrit were each coated onto fiber discs using the CaCO₃ filled make,cryolite filled size and KBF₄ filled supersize. Three discs for eachexample were evaluated on the Swing Arm Grinder using a flat test togrind stainless steel discs. The average grinding performance of theExample 6, Comparative Example H, and Comparative Example I coatedabrasive articles were 108%, 100%, 110% of Comparative Example H,respectively.

Distinct laminar layers in the co-extruded material could not bedetected by SEM or x-ray microanalysis, possibly due to the migration ofzirconium during drying.

Example 7 and Comparative Examples J and K

Example 7 and Comparative Examples J and K abrasive grit materials wereprepared as described for Example 1 and Comparative Examples A and Bexcept as follows. For Example 7, Sols V and VI were used in place ofSols I and II. For Comparative Example J, Sol V was used in place of SolI. For Comparative Example K, Sol VI was used in place of Sol II.Further, the calcined materials were not impregnated with the rare earthnitrate solution, and were sintered at 1430° C. in the rotary kiln.

For each of Example 7 and Comparative Examples J and K the sinteredmaterials were screened and blended to provide, by weight, 8.4 grams-25+30 mesh, 5.7 grits -30+35 mesh, and 1.8 grams -35+40 mesh abrasivegrit. The resulting mixtures were each blended with 21 grams of Grade 24brown fused alumina (obtained from Washington Mills, and then rollcrushed and screened). Each blend was used to make three coated abrasivediscs having about 12.3 grams of abrasive grit on each disc. The resinsused to make the discs were the CaCO₃ make and the cryolite size.

The discs were ground by a slide action grinder, with grinding fortwenty one-minute intervals using 1018 mild steel workpiece, and theload was 6 kilograms (13 lbs.). The average total cut of the Example 7and Comparative Examples J and K coated abrasive discs were 1005.4grams, 1216.2 grams, and 973.4 grams, respectively. The averagemicrohardness of the Example 7 and Comparative Examples J and Kmaterials, based on measurements on cross-section of the rods, were 17.9GPa, 19.6 GPa, and 17.8 GPa, respectively.

Example 8 and Comparative Examples L and M

Example 8 and Comparative Examples L and M abrasive grit were preparedas described for Example I and Comparative Examples A and B,respectively, except as follows. For Example 8, Sols I and VII were usedin place of Sols I and II. For Example L, Sol I was used. ForComparative Example M, Sol VII was used in place of Sol II. Oncecalcined at 650° C., the rods were impregnated with the rare earth oxidesolution, but were sintered at 1410° C. in the rotary kiln.

The average microhardness of cross-sections of the sintered Example 8and Comparative Example L and M (rod) material were 17.8 GPa, 17.9 GPaand 17.0 GPa, respectively.

The sintered rods were crushed and screened as described in Example 1.Those rods retained on the 30 and 35 mesh screens were blended at a50%/50% weight ratio of -30+35 mesh and -25+30 mesh material. Theresulting -25+30/-30+35 mesh blend was mixed with an equal weight ofANSI grade 24 brown fused alumina obtained as described above. The blendwas used to make four discs of each lot with each lot containing 12grams of mineral per disc. The resins used to make the discs were theCaCO₃ make, cryolite size and KBF₄ supersize. The discs were ground asdescribed in Example 7 and Comparative Examples J and K except grindingwas for ten minutes at one minute intervals using 304 stainless steelworkpieces, and the load was 6 kilograms (13 lbs.). The average totalcut of the Example 8 and Comparative Example L and M coated abrasivediscs were 165.4 grams, 159.2 grams, and 167.8 grams, respectively.

X-ray mapping indicated alternating Ce-rich layer. This example thusshowed that ceria could be successfully incorporated by co-extrusionwithout significant migration into the other phase.

Illustrative Example 1 and Comparative Examples N and O

A 9.1% aluminum formoacetate (AFA) solution was prepared as outlined inby Richards, Goodbrake and Sowman, J. Am. Ceram. Soc., 74, [10 ]2404-2409 (1991). The AFA solution was concentrated to 20.5% solids at40° C. using a vacuum rotary evaporator. The concentrated AFA solutionhad a thick, syrup-like, consistency.

Illustrative Example 1 and Comparative Examples N and O were prepared asdescribed in Example 1 and Comparative Examples A and B except asfollows. For Illustrative Example 1, Sol III and the concentrated AFAwere used in place of Sols I and II. For Comparative Example N, Sol IIIwas used in place of Sol I. For Comparative Example O the concentratedAFA was used in place of Sol II. The filled cartridges were capped andallowed to stand upside down so that the air would work its way to thetip of the cartridges. After the filled cartridges were allowed to standfor one week cartridges the contents were extruded into rods asdescribed before.

Upon drying, however, Comparative Example O rods disintegrated into afine powder, and was therefore not further processed. With regard toIllustrative Example 1, when Sol III and the concentrated AFA wereco-extruded, Sol III extruded out to resemble fine cottage cheese, whilethe AFA phase was runny and flowed. When the latter extruded material(i.e., the Sol III/AFA extruded material), a fine powder resulted, andwas not further processed.

This example shows the importance that viscosity plays with respect tothe co-extruded phases. If one phase, during co-extruding, is ofrelatively low viscosity and the other phase is of relatively highviscosity, the low viscosity phase will effectively flow around the highviscosity phase, during co-extrusion. What will likely result is thatthe high viscosity phase will form particles in the lower viscosityphase, providing a somewhat "cottage cheese" look. To avoid this, ingeneral the phases should be formulated with relatively similarviscosities.

What is claimed is:
 1. A ceramic abrasive grit comprising sintered,shaped, densified particles having at least three continuous andcontiguous, stratified, alumina-based layers of at least two differentphases.
 2. The ceramic abrasive grit of claim 1 wherein at least onelayer is seeded.
 3. The ceramic abrasive grit of claim 2 wherein atleast one layer contains an iron oxide seed or a precursor thereto. 4.The ceramic abrasive grit of claim 1 wherein at least one layercomprises zirconia.
 5. The ceramic abrasive grit of claim 1 wherein atleast one layer comprises ceria.
 6. The ceramic abrasive grit of claim 1wherein the grit further comprises modifiers.
 7. The ceramic abrasivegrit of claim 1 wherein the shaped particles are a random crushed shape.8. The ceramic abrasive grit of claim 1 wherein the shaped particles arerod-shaped.
 9. The ceramic abrasive grit of claim 1 wherein at least onelayer has two measured dimensions of at least 70 microns.
 10. Theceramic abrasive grit of claim 1 wherein at least one layer has twomeasured dimensions of at least 10 microns.
 11. The ceramic abrasivegrit of claim 1 wherein at least one layer extends at least 50% of agreatest dimension of width of the ceramic particle when viewed in atleast one selected cross-section.
 12. A coated abrasive articlecontaining a ceramic abrasive grit according to claim
 1. 13. A bondedabrasive article containing a ceramic abrasive grit according toclaim
 1. 14. A nonwoven abrasive article containing a ceramic abrasivegrit according to claim
 1. 15. An abrasive brush containing a ceramicabrasive grit according to claim 1.